Methods of Forming Conductive and Insulating Layers

ABSTRACT

Methods of forming conductive and insulating layers for semiconductor devices and packages. Substrate is provided with integrated circuit device and interconnect structure mounted thereon, the interconnect structure adjacent the integrated circuit device. The integrated circuit device and portions of the interconnect structure can be covered with an encapsulation exposing a portion of the interconnect structure. Conductive material is formed over the exposed portion of the interconnect structure by a depositing process followed by a heating process to alter the chemical properties of the conductive material. Optionally, a dispersing process may be incorporated.

CLAIM TO DOMESTIC PRIORITY

The present application is a continuation of U.S. patent applicationSer. No. 13/929,776, filed Jun. 27, 2013, which application isincorporated herein by reference.

FIELD OF THE INVENTION

The present disclosure relates in general to semiconductor devices and,more particularly, to methods of forming conductive and insulatinglayers for semiconductor devices and packages.

BACKGROUND OF THE INVENTION

Semiconductor devices are commonly found in modern electronic products.Semiconductor devices vary in the number and density of electricalcomponents. Discrete semiconductor devices generally contain one type ofelectrical component, e.g., light emitting diode (LED), small signaltransistor, resistor, capacitor, inductor, and power metal oxidesemiconductor field effect transistor (MOSFET). Integrated semiconductordevices typically contain hundreds to millions of electrical components.Examples of integrated semiconductor devices include microcontrollers,microprocessors, charged-coupled devices (CCDs), solar cells, anddigital micro-mirror devices (DMDs).

Semiconductor devices perform a wide range of functions such as signalprocessing, high-speed calculations, transmitting and receivingelectromagnetic signals, controlling electronic devices, transformingsunlight to electricity, and creating visual projections for televisiondisplays. Semiconductor devices are found in the fields ofentertainment, communications, power conversion, networks, computers,and consumer products. Semiconductor devices are also found in militaryapplications, aviation, automotive, industrial controllers, and officeequipment.

Semiconductor devices exploit the electrical properties of semiconductormaterials. The atomic structure of semiconductor material allows itselectrical conductivity to be manipulated by the application of anelectric field or base current or through the process of doping. Dopingintroduces impurities into the semiconductor material to manipulate andcontrol the conductivity of the semiconductor device.

A semiconductor device contains active and passive electricalstructures. Active structures, including bipolar and field effecttransistors, control the flow of electrical current. By varying levelsof doping and application of an electric field or base current, thetransistor either promotes or restricts the flow of electrical current.Passive structures, including resistors, capacitors, and inductors,create a relationship between voltage and current necessary to perform avariety of electrical functions. The passive and active structures areelectrically connected to form circuits, which enable the semiconductordevice to perform high-speed calculations and other useful functions.

Semiconductor devices are generally manufactured using two complexmanufacturing processes, i.e., front-end manufacturing, and back-endmanufacturing, each involving potentially hundreds of steps. Front-endmanufacturing involves the formation of a plurality of die on thesurface of a semiconductor wafer. Each semiconductor die is typicallyidentical and contains circuits formed by electrically connecting activeand passive components. Back-end manufacturing involves singulatingindividual semiconductor die from the finished wafer and packaging thedie to provide structural support and environmental isolation. The term“semiconductor die” as used herein refers to both the singular andplural form of the words, and accordingly can refer to both a singlesemiconductor device and multiple semiconductor devices.

One goal of semiconductor manufacturing is to produce smallersemiconductor devices. Smaller devices typically consume less power,have higher performance, and can be produced more efficiently. Inaddition, smaller semiconductor devices have a smaller footprint, whichis desirable for smaller end products. A smaller semiconductor die sizecan be achieved by improvements in the front-end process resulting insemiconductor die with smaller, higher density active and passivecomponents. Back-end processes may result in semiconductor devicepackages with a smaller footprint by improvements in electricalinterconnection and packaging materials.

SUMMARY OF THE INVENTION

Methods of forming conductive and insulating layers for semiconductordevices and packages are disclosed. In one embodiment, a method offorming conductive layers for semiconductor devices and packagesincludes (a) providing a substrate having an upper surface and a lowersurface, where the lower surface opposite the upper surface, and (b)mounting a first integrated circuit device over the upper surface of thesubstrate. Next, the method includes (c) mounting an interconnectstructure over the upper surface of the substrate, where theinterconnect structure adjacent the first integrated circuit device. Themounting steps (b) and (c) can be carried out concurrently, if desired.Next, the method includes (d) covering the first integrated circuitdevice and portions of the interconnect structure with an encapsulationmaterial leaving an upper portion of the interconnect structure exposed,followed by (e) forming a first conductive material over the upperportion of the interconnect structure and the encapsulation material. Inthis embodiment, the forming step (e) includes the following sub-steps:(i) depositing the first conductive material having a first state, and(ii) heating the first conductive material from the first state to asecond state, where the second state is different from the first state.

In one embodiment, the method further includes mounting a semiconductorpackage over the first conductive material, where the semiconductorpackage includes a second integrated circuit device. In anotherembodiment, the method further includes forming a plurality of externalinterconnects on the lower surface of the substrate, where the externalinterconnects are in communication with at least one of the firstintegrated circuit device and the second integrated circuit device. Inyet another embodiment, the method further includes treating the upperportion of the interconnect structure with a deflashing process afterthe covering step (d) but before the forming step (e).

In some embodiments, the depositing step (i) of the forming step (e)includes depositing the first conductive material including at least oneof silver (Ag), platinum (Pt), gold (Au), copper (Cu), carbon nanotube(CNT), graphene, organic metal, and mixtures thereof. In otherembodiments, the method further includes treating the upper portion ofthe interconnect structure with hydrophilic plasma prior to the formingstep (e). In one embodiment, the method further includes forming asecond conductive material over the first conductive material, where thesecond conductive material and the first conductive material havingsubstantially similar geometric footprint. In another embodiment, themethod further includes forming an isolating material over theencapsulation material, where a first portion of the isolating materialis formed over the first conductive material and the second conductivematerial, and where a second portion of the isolating material is formedin between and adjacent to the first conductive material and the secondconductive material.

In one embodiment, a method of forming conductive layers forsemiconductor devices and packages includes (a) providing a substratehaving an upper surface and a lower surface, where the lower surface isopposite the upper surface, (b) mounting a first integrated circuitdevice over the upper surface of the substrate, and (c) mounting aninterconnect structure over the upper surface of the substrate, wherethe interconnect structure is adjacent the first integrated circuitdevice. The mounting steps (b) and (c) can be carried out concomitantly.The method further includes (d) covering the first integrated circuitdevice and portions of the interconnect structure with an encapsulationmaterial leaving an upper portion of the interconnect structure exposed,and (e) forming a conductive material over the upper portion of theinterconnect structure and the encapsulation material. In oneembodiment, the forming step (e) includes the following sub-steps: (i)depositing the conductive material having a first state, and (ii)heating the conductive material from the first state to a second state,where the second state is different from the first state. The methodfurther includes (f) forming an isolating material over theencapsulation material, where a first portion of the isolating materialis formed over the conductive material, and where a second portion ofthe isolating material is formed in between and adjacent to theconductive material.

In one embodiment, the method further includes (g) mounting asemiconductor package over the conductive material and the isolatingmaterial, where the semiconductor package includes a second integratedcircuit device. In another embodiment, the method further includesforming a plurality of external interconnects on the lower surface ofthe substrate, where the external interconnects are in communicationwith at least one of the first integrated circuit device and the secondintegrated circuit device. In yet another embodiment, the method furtherincludes treating the upper portion of the interconnect structure with adeflashing process after the covering step (d) but before the formingstep (e).

In one embodiment, the forming step (f) includes forming the isolatingmaterial including at least one of dielectric ink, dielectric paste,thermosetting resin, and mixtures thereof. In another embodiment, themethod further includes treating the upper portion of the interconnectstructure with hydrophilic plasma prior to the forming step (e).

In one embodiment, a method of forming conductive layers forsemiconductor devices and packages includes (a) providing a substratehaving an upper surface and a lower surface, where the lower surface isopposite the upper surface, (b) mounting a first integrated circuitdevice over the upper surface of the substrate, and (c) mounting aninterconnect structure over the upper surface of the substrate, wherethe interconnect structure is adjacent the first integrated circuitdevice. Next, the method includes (d) covering a peripheral portion ofthe first integrated circuit device and a peripheral portion of theinterconnect structure with an encapsulation material leaving an uppersurface of the first integrated circuit device and an upper portion ofthe interconnect structure exposed, followed by (e) forming aninsulating material over the upper surface of the first integratedcircuit device. In one embodiment, the forming step (e) includes: (i)depositing the insulating material having a first state, and (ii)heating the insulating material from the first state to a second state,where the second state is different from the first state. Next, themethod includes (f) forming a first conductive material over theinsulating material extending from the upper surface of the firstintegrated circuit device to the upper portion of the interconnectstructure. In one embodiment, the forming step (f) includes: (i)depositing the first conductive material having a third state, and (ii)heating the first conductive material from the third state to a fourthstate, where the fourth state is different from the third state.

In one embodiment, the method further includes (g) mounting asemiconductor package over the first conductive material, where thesemiconductor package includes a second integrated circuit device. Inanother embodiment, the method further includes forming a plurality ofexternal interconnects on the lower surface of the substrate, where theexternal interconnects are in communication with at least one of thefirst integrated circuit device and the second integrated circuitdevice. In yet another embodiment, the method further includes treatingthe upper portion of the interconnect structure with a deflashingprocess after the forming step (e) but before the forming step (f).

In one embodiment, the depositing step (i) of the forming step (e)includes depositing the insulating material including at least one ofdielectric ink, dielectric paste, thermosetting resin, and mixturesthereof. In another embodiment, the depositing step (i) of the formingstep (f) includes depositing the first conductive material including atleast one of silver (Ag), platinum (Pt), gold (Au), copper (Cu), carbonnanotube (CNT), graphene, organic metal, and mixtures thereof. In oneembodiment, the method further includes treating the upper portion ofthe interconnect structure with hydrophilic plasma prior to the formingstep (f). In another embodiment, the method further includes (g) forminga second conductive material over the first conductive material, wherethe second conductive material and the first conductive material havesubstantially similar geometric footprint. In yet another embodiment,the method further includes (h) forming an isolating material over theupper surface of the first integrated circuit device, where a firstportion of the isolating material is formed over the first conductivematerial and the second conductive material, and where a second portionof the isolating material is formed in between and adjacent to the firstconductive material and the second conductive material.

In one embodiment, a method of forming conductive layers forsemiconductor devices and packages includes (a) providing a substratehaving an upper surface and a lower surface, where the lower surface isopposite the upper surface, (b) mounting a first integrated circuitdevice over the upper surface of the substrate, and (c) mounting aninterconnect structure over the upper surface of the substrate, wherethe interconnect structure is adjacent the first integrated circuitdevice. Next, the method includes (d) covering a peripheral portion ofthe first integrated circuit device and a peripheral portion of theinterconnect structure with an encapsulation material leaving an uppersurface of the first integrated circuit device and an upper portion ofthe interconnect structure exposed, followed by (e) forming aninsulating material over the upper surface of the first integratedcircuit device. In one embodiment, the forming step (e) includes thefollowing sub-steps: (i) depositing the insulating material having afirst state, and (ii) heating the insulating material from the firststate to a second state, where the second state is different from thefirst state. Next, the method includes (f) forming a conductive materialover the insulating material extending from the upper surface of thefirst integrated circuit device to the upper portion of the interconnectstructure. In this embodiment, the forming step (f) includes thefollowing sub-steps: (i) depositing the conductive material having athird state, and (ii) heating the conductive material from the thirdstate to a fourth state, where the fourth state is different from thethird state. Next, the method includes (g) forming an isolating materialover the upper surface of the first integrated circuit device, where afirst portion of the isolating material is formed over the conductivematerial, and where a second portion of the isolating material is formedin between and adjacent to the conductive material.

In one embodiment, the method further includes (h) mounting asemiconductor package over the conductive material and the isolatingmaterial, where the semiconductor package includes a second integratedcircuit device. In another embodiment, the method further includesforming a plurality of external interconnects on the lower surface ofthe substrate, where the external interconnects are in communicationwith at least one of the first integrated circuit device and the secondintegrated circuit device. In some embodiments, the method includestreating the upper portion of the interconnect structure with adeflashing process after the forming step (e) but before the formingstep (f). In other embodiments, the depositing step (i) of the formingstep (e) includes depositing the insulating material including at leastone of dielectric ink, dielectric paste, thermosetting resin, andmixtures thereof. In some embodiments, the forming step (g) includesforming the isolating material including at least one of dielectric ink,dielectric paste, thermosetting resin, and mixtures thereof. In otherembodiments, the method further includes treating the upper portion ofthe interconnect structure with hydrophilic plasma prior to the formingstep (f).

Other variations, embodiments and features of the present disclosurewill become evident from the following detailed description, drawingsand claims.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 illustrates a printed circuit board (PCB) with different types ofpackages mounted to its surface;

FIGS. 2a-2c illustrate further detail of the representativesemiconductor packages mounted to the PCB;

FIGS. 3a-3b illustrate details of a representative semiconductorsubstrate;

FIGS. 4-6 are top-down and cross-sectional views of a method of formingconductive layers on a semiconductor package according to oneembodiment;

FIG. 7 includes top-down and cross-sectional views of a semiconductorpackage according to one embodiment;

FIG. 8 includes top-down and cross-sectional views of a semiconductorpackage according to one embodiment;

FIG. 9 includes top-down and cross-sectional views of the package ofFIG. 6 with a different interconnect structure;

FIGS. 10-13 are top-down and cross-sectional views of a method offorming conductive and insulating layers on a semiconductor packageaccording to one embodiment;

FIG. 14 includes top-down and cross-sectional views of a semiconductorpackage according to one embodiment;

FIG. 15 includes top-down and cross-sectional views of a semiconductorpackage according to one embodiment;

FIG. 16 includes top-down and cross-sectional views of the package ofFIG. 13 with a different interconnect structure;

FIG. 17 is a cross-sectional view of a semiconductor package accordingto one embodiment; and

FIG. 18 is a flow diagram of the methods of forming conductive andinsulating layers on semiconductor devices and packages.

DETAILED DESCRIPTION OF THE DRAWINGS

It will be appreciated by those of ordinary skill in the art that theembodiments disclosed herein can be embodied in other specific formswithout departing from the spirit or essential character thereof. Thepresently disclosed embodiments are therefore considered in all respectsto be illustrative and not restrictive.

The present disclosure is described in one or more embodiments in thefollowing description with reference to the figures, in which likenumerals represent the same or similar elements. While the disclosure isdescribed in terms of the best mode for achieving the disclosure'sobjectives, it will be appreciated by those skilled in the art that itis intended to cover alternatives, modifications, and equivalents as maybe included within the spirit and scope of the disclosure as defined bythe appended claims and their equivalents as supported by the followingdisclosure and drawings.

Semiconductor devices are generally manufactured using two complexmanufacturing processes: front-end manufacturing and back-endmanufacturing. Front-end manufacturing involves the formation of aplurality of die on the surface of a semiconductor wafer. Each die onthe wafer contains active and passive electrical components, which areelectrically connected to form functional electrical circuits. Activeelectrical components, such as transistors and diodes, have the abilityto control the flow of electrical current. Passive electricalcomponents, such as capacitors, inductors, resistors, and transformers,create a relationship between voltage and current necessary to performelectrical circuit functions.

Passive and active components are formed over the surface of thesemiconductor wafer by a series of process steps including doping,deposition, photolithography, etching, and planarization. Dopingintroduces impurities into the semiconductor material by techniques suchas ion implantation or thermal diffusion. The doping process modifiesthe electrical conductivity of semiconductor material in active devices,transforming the semiconductor material into an insulator, conductor, ordynamically changing the semiconductor material conductivity in responseto an electric field or base current. Transistors contain regions ofvarying types and degrees of doping arranged as necessary to enable thetransistor to promote or restrict the flow of electrical current uponthe application of the electric field or base current.

Active and passive components are formed by layers of materials withdifferent electrical properties. The layers can be formed by a varietyof deposition techniques determined in part by the type of materialbeing deposited. For example, thin film deposition can involve chemicalvapor deposition (CVD), physical vapor deposition (PVD), electrolyticplating, and electroless plating processes. Each layer is generallypatterned to form portions of active components, passive components, orelectrical connections between components.

The layers can be patterned using photolithography, which involves thedeposition of light sensitive material, e.g., photoresist, over thelayer to be patterned. A pattern is transferred from a photomask to thephotoresist using light. In one embodiment, the portion of thephotoresist pattern subjected to light is removed using a solvent,exposing portions of the underlying layer to be patterned. In anotherembodiment, the portion of the photoresist pattern not subjected tolight, i.e., the negative photoresist, is removed using a solvent,exposing portions of the underlying layer to be patterned. The remainderof the photoresist is removed, leaving behind a patterned layer.Alternatively, some types of materials are patterned by directlydepositing the material into the areas or voids formed by a previousdeposition/etch process using techniques such as electroless andelectrolytic plating.

Patterning is the basic operation by which portions of the top layers onthe semiconductor wafer surface are removed. Portions of thesemiconductor wafer can be removed using photolithography, photomasking,masking, oxide or metal removal, photography and stenciling, andmicrolithography. Photolithography includes forming a pattern inreticles or a photomask and transferring the pattern into the surfacelayers of the semiconductor wafer. Photolithography forms the horizontaldimensions of active and passive components on the surface of thesemiconductor wafer in a two-step process. First, the pattern on thereticle or masks is transferred into a layer of photoresist. Photoresistis a light-sensitive material that undergoes changes in structure andproperties when exposed to light. The process of changing the structureand properties of the photoresist occurs as either negative-actingphotoresist or positive-acting photoresist. Second, the photoresistlayer is transferred into the wafer surface. The transfer occurs whenetching removes the portion of the top layers of semiconductor wafer notcovered by the photoresist. The chemistry of photoresists is such thatthe photoresist remains substantially intact and resists removal bychemical etching solutions while the portion of the top layers of thesemiconductor wafer not covered by the photoresist is removed. Theprocess of forming, exposing, and removing the photoresist, as well asthe process of removing a portion of the semiconductor wafer can bemodified according to the particular resist used and the desiredresults.

In negative-acting photoresists, photoresist is exposed to light and ischanged from a soluble condition to an insoluble condition in a processknown as polymerization. In polymerization, unpolymerized material isexposed to a light or energy source and polymers form a cross-linkedmaterial that is etch-resistant. In most negative resists, the polymersare polyisopremes. Removing the soluble portions (i.e. the portions notexposed to light) with chemical solvents or developers leaves a hole inthe resist layer that corresponds to the opaque pattern on the reticle.A mask whose pattern exists in the opaque regions is called aclear-field mask.

In positive-acting photoresists, photoresist is exposed to light and ischanged from relatively nonsoluble condition to much more solublecondition in a process known as photosolubilization. Inphotosolubilization, the relatively insoluble resist is exposed to theproper light energy and is converted to a more soluble state. Thephotosolubilized part of the resist can be removed by a solvent in thedevelopment process. The basic positive photoresist polymer is thephenol-formaldehyde polymer, also called the phenol-formaldehyde novolakresin. Removing the soluble portions (i.e. the portions exposed tolight) with chemical solvents or developers leaves a hole in the resistlayer that corresponds to the transparent pattern on the reticle. A maskwhose pattern exists in the transparent regions is called a dark-fieldmask.

After removal of the top portion of the semiconductor wafer not coveredby the photoresist, the remainder of the photoresist is removed, leavingbehind a patterned layer. Alternatively, some types of materials arepatterned by directly depositing the material into the areas or voidsformed by a previous deposition/etch process using techniques such aselectroless and electrolytic plating.

Depositing a thin film of material over an existing pattern canexaggerate the underlying pattern and create a non-uniformly flatsurface. A uniformly flat surface is required to produce smaller andmore densely packed active and passive components. Planarization can beused to remove material from the surface of the wafer and produce auniformly flat surface. Planarization involves polishing the surface ofthe wafer with a polishing pad. An abrasive material and corrosivechemical are added to the surface of the wafer during polishing. Thecombined mechanical action of the abrasive and corrosive action of thechemical removes any irregular topography, resulting in a uniformly flatsurface.

Back-end manufacturing refers to cutting or singulating the finishedwafer into the individual semiconductor die and then packaging thesemiconductor die for structural support and environmental isolation. Tosingulate the semiconductor die, the wafer is scored and broken alongnon-functional regions of the wafer called saw streets or scribes. Thewafer is singulated using a laser cutting tool or saw blade. Aftersingulation, the individual semiconductor die are mounted to a packagesubstrate that includes pins or contact pads for interconnection withother system components. Contact pads formed over the semiconductor dieare then connected to contact pads within the package. The electricalconnections can be made with solder bumps, stud bumps, conductive paste,or wirebonds. An encapsulant or other molding material is deposited overthe package to provide physical support and electrical isolation. Thefinished package is then inserted into an electrical system and thefunctionality of the semiconductor device is made available to the othersystem components.

FIG. 1 illustrates electronic device 50 having a chip carrier substrateor printed circuit board (PCB) 52 with a plurality of semiconductorpackages mounted on its surface. Electronic device 50 can have one typeof semiconductor package, or multiple types of semiconductor packages,depending on the application. The different types of semiconductorpackages are shown in FIG. 1 for purposes of illustration.

Electronic device 50 can be a stand-alone system that uses thesemiconductor packages to perform one or more electrical functions.Alternatively, electronic device 50 can be a subcomponent of a largersystem. For example, electronic device 50 can be part of a cellularphone, personal digital assistant (PDA), digital video camera (DVC), orother electronic communication device. Alternatively, electronic device50 can be a graphics card, network interface card, or other signalprocessing card that can be inserted into a computer. The semiconductorpackage can include microprocessors, memories, application specificintegrated circuits (ASIC), logic circuits, analog circuits, RFcircuits, discrete devices, or other semiconductor die or electricalcomponents. Miniaturization and weight reduction are essential for theseproducts to be accepted by the market. The distance betweensemiconductor devices must be decreased to achieve higher density.

In FIG. 1, PCB 52 provides a general substrate for structural supportand electrical interconnect of the semiconductor packages mounted on thePCB. Conductive signal traces 54 are formed over a surface or withinlayers of PCB 52 using evaporation, electrolytic plating, electrolessplating, screen printing, or other suitable metal deposition process.Signal traces 54 provide for electrical communication between each ofthe semiconductor packages, mounted components, and other externalsystem components. Traces 54 also provide power and ground connectionsto each of the semiconductor packages.

In some embodiments, a semiconductor device has two packaging levels.First level packaging is a technique for mechanically and electricallyattaching the semiconductor die to an intermediate carrier. Second levelpackaging involves mechanically and electrically attaching theintermediate carrier to the PCB. In other embodiments, a semiconductordevice may only have the first level packaging where the die ismechanically and electrically mounted directly to the PCB.

For the purpose of illustration, several types of first level packaging,including bond wire package 56 and flipchip 58, are shown on PCB 52.Additionally, several types of second level packaging, including ballgrid array (BGA) 60, bump chip carrier (BCC) 62, dual in-line package(DIP) 64, land grid array (LGA) 66, multi-chip module (MCM) 68, quadflat non-leaded package (QFN) 70, and quad flat package 72, are shownmounted on PCB 52. Depending upon the system requirements, anycombination of semiconductor packages, configured with any combinationof first and second level packaging styles, as well as other electroniccomponents, can be connected to PCB 52. In some embodiments, electronicdevice 50 includes a single attached semiconductor package, while otherembodiments call for multiple interconnected packages. By combining oneor more semiconductor packages over a single substrate, manufacturerscan incorporate pre-made components into electronic devices and systems.Because the semiconductor packages include sophisticated functionality,electronic devices can be manufactured using less expensive componentsand a streamlined manufacturing process. The resulting devices are lesslikely to fail and less expensive to manufacture resulting in a lowercost for consumers.

FIGS. 2a-2c show exemplary semiconductor packages. FIG. 2a illustratesfurther detail of DIP 64 mounted on PCB 52. Semiconductor die 74includes an active region containing analog or digital circuitsimplemented as active devices, passive devices, conductive layers, anddielectric layers formed within the die and are electricallyinterconnected according to the electrical design of the die. Forexample, the circuit can include one or more transistors, diodes,inductors, capacitors, resistors, and other circuit elements formedwithin the active region of semiconductor die 74. Contact pads 76 areone or more layers of conductive material, such as aluminum (Al), copper(Cu), tin (Sn), nickel (Ni), gold (Au), or silver (Ag), and areelectrically connected to the circuit elements formed withinsemiconductor die 74. During assembly of DIP 64, semiconductor die 74 ismounted to an intermediate carrier 78 using a gold-silicon eutecticlayer or adhesive material such as thermal epoxy or epoxy resin. Thepackage body includes an insulative packaging material such as polymeror ceramic. Conductor leads 80 and bond wires 82 provide electricalinterconnect between semiconductor die 74 and PCB 52. Encapsulant 84 isdeposited over the package for environmental protection by preventingmoisture and particles from entering the package and contaminatingsemiconductor die 74 or bond wires 82.

FIG. 2b illustrates further detail of BCC 62 mounted on PCB 52.Semiconductor die 88 is mounted over carrier 90 using an underfill orepoxy-resin adhesive material 92. Bond wires 94 provide first levelpackaging interconnect between contact pads 96 and 98. Molding compoundor encapsulant 100 is deposited over semiconductor die 88 and bond wires94 to provide physical support and electrical isolation for the device.Contact pads 102 are formed over a surface of PCB 52 using a suitablemetal deposition process such as electrolytic plating or electrolessplating to prevent oxidation. Contact pads 102 are electricallyconnected to one or more conductive signal traces 54 in PCB 52. Bumps104 are formed between contact pads 98 of BCC 62 and contact pads 102 ofPCB 52.

In FIG. 2c , semiconductor die 58 is mounted face down to intermediatecarrier 106 with a flipchip style first level packaging. Active region108 of semiconductor die 58 contains analog or digital circuitsimplemented as active devices, passive devices, conductive layers, anddielectric layers formed according to the electrical design of the die.For example, the circuit can include one or more transistors, diodes,inductors, capacitors, resistors, and other circuit elements withinactive region 108. Semiconductor die 58 is electrically and mechanicallyconnected to carrier 106 through bumps 110.

BGA 60 is electrically and mechanically connected to PCB 52 with a BGAstyle second level packaging using bumps 112. Semiconductor die 58 iselectrically connected to conductive signal traces 54 in PCB 52 throughbumps 110, signal lines 114, and bumps 112. A molding compound orencapsulant 116 is deposited over semiconductor die 58 and carrier 106to provide physical support and electrical isolation for the device. Theflipchip semiconductor device provides a short electrical conductionpath from the active devices on semiconductor die 58 to conductiontracks on PCB 52 in order to reduce signal propagation distance, lowercapacitance, and improve overall circuit performance. In anotherembodiment, the semiconductor die 58 can be mechanically andelectrically connected directly to PCB 52 using flipchip style firstlevel packaging without intermediate carrier 106.

FIG. 3a shows a semiconductor wafer 120 with a base substrate material122, such as silicon, germanium, gallium arsenide, indium phosphide, orsilicon carbide, for structural support. A plurality of semiconductordie or components 124 is formed on wafer 120 separated by a non-active,inter-die wafer area or saw street 126 as described above. Saw street126 provides cutting areas to singulate semiconductor wafer 120 intoindividual semiconductor die 124.

FIG. 3b shows a cross-sectional view of a portion of semiconductor wafer120. Each semiconductor die 124 has a back surface 128 and activesurface 130 containing analog or digital circuits implemented as activedevices, passive devices, conductive layers, and dielectric layersformed within the die and electrically interconnected according to theelectrical design and function of the die. For example, the circuit mayinclude one or more transistors, diodes, and other circuit elementsformed within active surface 130 to implement analog circuits or digitalcircuits, such as digital signal processor (DSP), ASIC, memory, or othersignal processing circuit. Semiconductor die 124 may also containintegrated passive devices (IPDs), such as inductors, capacitors, andresistors, for RF signal processing.

FIGS. 4-6 are top-down and cross-sectional views of a method of formingconductive layers on a semiconductor package 300 according to oneembodiment of the present disclosure. FIG. 4 includes a top-down view ofthe semiconductor package 300 with a cross-sectional view through A-A ofthe semiconductor package 300. As shown, the package 300 includes asubstrate 106 having an upper surface 142 and a lower surface 152. Inthis instance, the lower surface 152 is opposite the upper surface 142.The substrate 106 can be a semiconductor wafer or a chip carrier similarto those described above. For example, the substrate 106 can belaminate, printed circuit board (PCB), silicon, organic, ceramic,plastic or some other laminated or flexible structure for redistributionof signals. In some embodiments, the substrate 106 can be a siliconwafer, an interposer or a redistribution material, among other suitablesemiconductor substrates.

An integrated circuit device 58 can be mounted on or attached to theupper surface 142 of the substrate 106 via a plurality of internalconnectors or bumps 110. The internal connectors 110 may be solderbumps, solder balls, copper pillars, copper balls, among others. Thebumps 110 may be underfilled or encapsulated with a molding compound 126such as an epoxy resin material, along with portions of the lowersurface of the integrated circuit device 58 facing the substrate 106.The process of forming the encapsulation 126 can be carried out usingfilm-assisted molding, epoxy molding, moldable underfill or otherprotective molding process. The encapsulation 126 can protect theintegrated circuit 58 as well as the bumps 110 from moisture, dust andother contaminants. In some embodiments, the molding compound 126 may beoptional leaving the bumps 110 as well as the lower surface of theintegrated circuit device 58 substantially open or exposed to theelements. In other embodiments, the integrated circuit device 58 can beattached to the upper surface 142 of the substrate 106 via an adhesivematerial.

In addition, interconnect structures 170 can be formed on the substrate106 to function as conductive signal connectors. In some embodiments,the interconnect structures 170 can be solder balls, solder bumps, studbumps, conductive pillars or other conductive structures. In otherembodiments, the interconnect structures 170 can be solder balls havingchemical compositions including without limitation tin, lead, silver,copper and nickel, or combinations thereof.

In one embodiment, the interconnect structures 170 and the integratedcircuit device 58 can be formed on the substrate 106 adjacent eachother. As shown, the interconnect structures 170 can be formed on bothsides of the integrated circuit device 58 although it is possible thatthe interconnect structures 170 can be formed on only one side of theintegrated circuit device 58 or can be otherwise configured per designspecifications. The integrated circuit device 58 can be formed on thesubstrate 106 before or after the formation of the interconnectstructures 170. In the alternative, the integrated circuit device 58 canbe formed concomitant (concurrently or at the same time) as theformation of the interconnect structures 170. The integrated circuitdevice 58 can be a flip chip, a wire-bond chip or other suitablesemiconductor device. In some embodiments, other types of integratedcircuit devices 58 including logic, memory, passives, among others, canalso be included.

In one embodiment, the interconnect structures 170 can include a corematerial 140 surrounded. by an outer layer 145. In this embodiment, theinterconnect structure 170 may include a core material 140 having aconductive copper or non-conductive polymeric material surrounded by anouter layer 145 of solder material, where the overall structure 140, 145is capable of providing better solder joint-ability, wettability,solderability, among other benefits. In one embodiment, theinterconnectstructure 170 may include a core material 140 made of metalcopper with a diameter of from about 100 to about 300 microns, and theouter layer 145 may include a thin nickel material with a film thicknessof from about 1 to about 4 microns. Optionally, the outer layer 145 mayinclude a solder material with a film thickness of from about 10 toabout 30 microns. Although bi-layer or tri-layer interconnect structures170 are disclosed, single material interconnect structures 170 includingthe likes of solder balls or solder bumps may also be used.

In one embodiment, a plurality of external interconnects 112 can beformed on the lower surface 152 of the substrate 106. The externalinterconnects 112 can be in electrical communication with the integratedcircuit device 58 through signal lines (not shown) in the substrate 106.The external interconnects 112 can also be in electrical communicationwith the integrated circuit device 58 through other suitable featuresincluding the likes of through-silicon vias (not shown), among others.The external interconnects 112 can also be in electrical communicationwith other features of the package 300 and will become more apparent insubsequent figures and discussion. The external interconnects 112 can beformed in similar manner and with similar material as that of theinterconnect structures 170. In one embodiment, the externalinterconnects 112 can be solder bumps formed on the lower surface 152 ofthe substrate 106 opposite the integrated circuit device 58 and theinterconnect structures 170.

In one embodiment, the integrated circuit device 58 and portions of theinterconnect structures 170 can be covered with an encapsulationmaterial 136, the encapsulation material 136 being similar to theencapsulation 126. An upper portion 190 of the interconnect structures170 may be exposed for subsequent processing. The encapsulation material136 can be formed using film-assisted molding, epoxy molding, moldableunderfill or other suitable molding process. Additional details on thefilm-assisted molding process are disclosed in U.S. Pat. No. 8,035,235granted Oct. 11, 2011 and filed as U.S. patent application Ser. No.12/560,312 on Sep. 15, 2009, which is hereby incorporated by referencein its entirety for all purposes.

In using film-assisted molding, because of the height difference betweenthe upper portion 190 of the interconnect structures 170 and the uppersurface of the integrated circuit die 58, only the interconnectstructures 170 are ph sically engaged to a mold chase having a film.Once inphysical contact, the voids or spaces created between thefilm/mold chase and the interconnect structures 170 can be filled ormolded with an encapsulation material 136 similar to that of theencapsulation 126. And although shown as two distinct layers 126, 136,it is also possible to integrate the encapsulation 126 and theencapsulation material 136 as a single layer in other words, the earlierencapsulation 126 can be eliminated and the entire package 300 can becovered or encapsulated with the encapsulation material 136 during thissubsequent step. In other embodiments, the encapsulation material 136may be solder resist or dielectric material formed by deposition,lithography and etching, among other suitable techniques.

In one embodiment, if the interconnect structure 170 includes a corematerial 140 and an outer layer 145, where the core material 140 ismetal copper ball with nickel plating, and the outer layer 145 is solderplated material, the core material 140 may be exposed after thefilm-assisted molding process. This may occur as a result of theinteractions between the interconnect structure 170 and theencapsulation material 136 as well as the film used in the mold chaseduring the film-assisted molding process. In other words, the upperportion 190 of the interconnect structure 170 may be the core material140. In another embodiment, the core material 140 may not be exposedduring the film-assisted molding process and the upper surface 190 ofthe interconnect structure 170 may be the outer layer 145.

FIG. 5 includes a top-down view of the next step in the manufacturingprocess of the semiconductor package 300 with a cross-sectional viewthrough A-A of the semiconductor package 300. In one embodiment, theupper portions 190 of the interconnect structures 170A, 170B, 170C, 170Dmay be treated with a deflashing process for cleaning purposes, amongother reasons, while other interconnect structures 170E, 170F may not besubject to a deflashing process. In other words, the deflashing processcan be selective. The deflashing process includes solder deflash as wellas laser deflash, among other suitable deflashing techniques. In oneembodiment, the deflashing process can take place on the solder or outerlayer 145 of the selected interconnect structures 170A, 170B, 170C,170D. In another embodiment, the deflashing process can take place onthe metal core material 140 of the selected interconnect structures170A, 170B, 170C, 170D. In some embodiments, the interconnect structures170 need not be selectively deflashed but instead all the interconnectstructures 170 can be subjected to a deflashing process.

FIG. 6 includes a top-down view of the next step in the manufacturingprocess of the semiconductor package 300 with a cross-sectional viewthrough A-A of the semiconductor package 300. In one embodiment, aconductive material 160 may be formed over the upper portion 190 of theinterconnect structures 170 as well as the encapsulation material 136.The conductive material 160 formed over the encapsulation material 136may extend over and into the areas above the integrated circuit device58 as best illustrated in the top-down view.

In some embodiments, the conductive material 160 can be formed by adirect writing process including the likes of screen printing orelectro-hydro dynamic (EHD) dispensing. Screen printing involves the useof a paste material, screen mesh, an emulsion material and applicationof force via an applicator with the substrate held by a nest. In thealternative, EHD dispensing involves the use of an electric field todispense droplets from a nozzle. In other embodiments, formation of theconductive material 160 can include the likes of inkjet printing, whichcan be continuous or on demand, and can be carried out in vertical orhorizontal fashion. The use of inkjet printing to form the conductivematerial 160 may provide visible and conductive metal lines that arehalogen free. The ink material that is involved may be of an organicmetal or a silver complex.

With inkjet printing, an inkjet head may be provided over the desiredarea of interest. In this instance, over the upper portions 190 of theinterconnect structures 170 as well as the trace lines (e.g., linesconnecting interconnect structures 170). The inkjet head can deliver aresolution of 1,200 dots per inch (DPI) although other inkjet heads withother resolution may be utilized. Upon passing over the desired area, anozzle from the inkjet head may cause an inkjet droplet to be depositedonto the upper portions 190 of the interconnect structures 170 as wellas the trace lines. The inkjet droplet, containing the ink material,will subsequently be formed into the desired conductive material layer160. In this example, the deposition can be accomplished via gravity. Inother instances, the deposition can be carried out via other suitablemechanical and/or electrical assistance including the likes of anelectric field, for example.

The number of nozzles on the inkjet head can vary. For example, therecan be a total of 2,048 nozzles providing coverage width of about 43millimeters. The nozzles and the head may have a writing speed of about200 millimeters per second. The number of droplets can be varieddepending on the desired thickness and/or width of the conductivematerial 160 to be achieved. For example, the number of droplets canvary between about 1 droplet to about 10 droplets, or greater than 10droplets. The inkjet droplet may have a diameter of anywhere from about3 microns to about 12 microns depending on the viscosity and the volumeof the ink being consumed. Meanwhile, the thickness of the conductivematerial 160 formed may be about 3 microns thick, or thinner than 3microns, or thicker than 3 microns. In this instance, the amount of inkcan be about 1 picoliter. Because of the plurality of nozzles and thespeed at which the head can process a substrate, inkjet printingthroughput can be on the matter of seconds per strip of devices.

In one embodiment, the inkjet droplet may be a conductive material 160in ink or liquid form. The types of conductive material 160 that can bein liquid or ink form include silver (Ag), platinum (Pt), gold (Au),copper (Cu), carbon nanotube (CNT), graphene, organic metal, or mixturesthereof. In another embodiment, the inkjet droplet that ultimately formsthe conductive layer 160 may be a conductive polymeric material withmetallic properties.

In another embodiment, instead of using inkjet printing and inkjetdroplet, conductive material 160 may be deposited in paste form and thatdeposition can be made by screen printing or EHD dispensing. The pastemay have material properties similar to the inkjet droplet disclosedabove including without limitation silver (Ag) paste, platinum (Pt)paste, gold (Au) paste or copper (Cu) paste, to name a few.

In one embodiment, prior to the deposition of the inkjet droplet, theupper portions 190 of the interconnect structures 170, as well as thetrace lines, may be treated with hydrophilic plasma. Treating the upperportions 190 of the interconnect structures 170 as well as the tracelines with hydrophilic plasma may raise the surface energy of the upperportions 190 of the interconnect structures 170 and the trace linesleading to increased dispersion of the conductive ink.

The inkjet droplet, once sitting on the upper portions 190 of theinterconnect structures 170 and the trace lines, can be allowed todisperse and spread out. Because of the low viscosity (<100 centipoise),the inkjet droplet is able to spread out to cover the desired surfacearea. For example, the inkjet droplet may have an initial area upondeposition. In one example, the initial area may be in the range of fromabout 10-15 microns (e.g., diameter of the droplet). In time, the inkjetdroplet may disperse or be allowed to disperse thereby arriving at afinal area. In one embodiment, the final area is greater than theinitial area. The final area may be substantially similar to the openingof the upper portion 190 of the interconnect structure 170. For example,the interconnect structure 170 may have a width of about 250 microns,with 200 microns being the final area or width (e.g., exposed upperportion 190) that the inkjet droplet may disperse. In other words, theinitial area may be about 15 microns while the final area may be about200 microns. The dispersion of more than 10-fold can be accomplishedbecause of the low viscosity of the inkjet droplet. The dispersion maybe further enhanced if the upper portions 190 of the interconnectstructures 170 and the trace lines had been subjected to the hydrophilicplasma process as discussed above, which helps to raise the surfaceenergy and enhance the dispersion process.

In operation, formation of the conductive material 160 over the upperportion 190 of the interconnect structure 170 includes depositing theconductive material 160, and optionally allowing the conductive material160 to disperse from an initial area to a final area. As indicatedabove, the final area can be greater than the initial area. Next,heating or curing the conductive material 160 into a solid form. Ifscreen printing or EHD dispensing is utilized, the conductive liquid orpaste may be deposited having a first material state, where the firstmaterial state includes liquid, viscous or paste form. The conductiveliquid or paste need not go through the dispersion or spreading processand a desired profile of the conductive material 160 may be formed afterthe deposition step. Next, the conductive material 160 can be heatedfrom the first material state to a second material state, where thesecond material state is different from the first material state. Thesecond material state may include solid, crystal or sintered form.

In some embodiments, after deposition and/or dispersion of theconductive material 160, a heating process may be carried out to furthersinter the material. In one embodiment, the heating process may includeoven or ultra-violet curing or both. The heating process may alsoinclude a reflow process for purposes of sintering the conductiveparticles that are in the conductive ink or paste material 160. In otherembodiments, the first state may have an initial profile while thesecond state may have a final profile where the final profile isdifferent from the initial profile. The difference in the profile may bea result of the heating or curing process which may drive out the fluidor viscous material in the liquid or paste causing the conductivematerial to undergo shrinkage into a more solid or sintered form. Theconductive ink, paste or liquid used in the formation of the conductivematerial 160 may include silver (Ag) complexes, platinum (Pt) complexes,gold (Au) complexes, copper (Cu) complexes, carbon nanotube (CNT),graphene, organic metal, or additives and mixtures thereof. Theconductive ink, paste or liquid may also be an organic polymer withmetallic properties.

In short, the conductive material 160 can be formed without alithographic process involving the coating and removal of a photoresistmaterial. Furthermore, the conductive material 160 can be formed withoutthe use of a traditional metallization process in which the material isdeposited and formed as is.

FIG. 7 includes top-down view of a semiconductor package 400 with across-sectional view through A-A of the semiconductor package 400, whichcan be continued from the semiconductor package 300 of FIG. 6 withadditional processing steps. In one embodiment, a second conductivematerial 260 can be formed over the first conductive material 160, wherethe second conductive material 260 and the first conductive material 160have substantially similar geometric footprint. In this embodiment, thegeometric layout of the second conductive layer 260 can follow those ofthe first conductive layer 160 as seen from the top-view as well as thecross-sectional view.

In one embodiment, the first conductive material 160 can serve as a seedlayer while the second conductive material 260 can be the conductivepattern to provide the conductive trace lines along with full area arraytop ball pads. The seed layer 160 may be formed as a conductive ink orpaste by direct writing including without limitation inkjet printing,screen printing or EHD dispensing, the formation being carried outwithout the use of photolithography and/or removal of photoresist.Further, the formation can be carried out without any etching of theconductive material 160. In some embodiments, the second conductivematerial 260 can be formed by electroplating or electro-less plating. Inother embodiments, the second conductive material 260 can be formed bythe printing processes described above similar to those for the firstconductive material 160.

FIG. 8 includes top-down view of a semiconductor package 500 with across-sectional view through A-A of the semiconductor package 500, whichcan be continued from the semiconductor package 300 of FIG. 6 withadditional processing steps. In one embodiment, an isolating material236 can be formed over the encapsulation material 136. In this instance,a first portion of the isolating material 236 can be formed over theconductive material 160 while a second portion of the isolating material236 can be formed in between and adjacent the conductive material 160.In general, the first portion of the isolating material 236 formed overthe conductive material 160 are more directed to the trace lines, e.g.,the conductive lines coupling the interconnect structures 170 to the toppads over the integrated circuit device 58. The second portion of theisolating material 236 formed in between and adjacent the conductivematerial 160 are those adjacent and in between the interconnectstructures 170 about the peripheral of the package 500. This is bestillustrated on the two peripheral sides of the cross-sectional view.

In one embodiment, the isolating material 236 includes at least one ofdielectric ink, dielectric paste, thermosetting resin, and mixturesthereof. In some embodiments, the isolating material 236 can be formedwith similar techniques as those above for the conductive material 160.For example, the isolating material 236 can be initially deposited,optionally be allowed to disperse or spread, and subsequently heated toform the desired structure and final profile. In other embodiments, theisolating material 236 can be solder mask material formed byphotolithography or direct writing with dielectric ink. Although shownto be formed over only one conductive layer 160, the package 400 of FIG.7 can be combined with the current package 500 such that the isolatingmaterial 236 can be formed over the encapsulation material 136 where aportion is over both conductive materials 160, 260 while another portionis in between and adjacent to. In some examples, the isolating material236, formed of the isolating material in ink, paste, or liquid form, canbe conformally formed over the structures underneath. In other words,the isolating material 236 can follow the shape or contour of theconductive layers 160, 260 including any angles and crevices thereof,and fill in any of such openings or recesses as necessary in forming theisolating layer 236.

FIG. 9 includes top-down view of a semiconductor package 350 with across-sectional view through A-A of the semiconductor package 350, whichis in essence substantially similar to the semiconductor package 300 ofFIG. 6 with the exception that the interconnect structure 170 includes asingle layer 144. In this package 350, the interconnect structure 170 isa standard solder ball with only a single core layer 144. There is noouter layer in this example. The interconnect structure 170 can beformed by traditional solder ball formation techniques. Furthermore, theinterconnect structure 170 can be implemented in other packages 400, 500as well.

FIGS. 10-13 are top-down and cross-sectional views of a method offorming conductive and insulating layers on a semiconductor package 600according to one embodiment of the present disclosure. FIG. 10 includesa top-down view of the semiconductor package 600 with a cross-sectionalview through A-A of the semiconductor package 600. As shown, the package600 includes a substrate 106 having an upper surface 142 and a lowersurface 152 similar to that discussed above. An integrated circuitdevice 58 can be mounted over the upper surface 142 of the substrate 106via a plurality of internal connectors 110 and encapsulated with amolding compound 126. A plurality of interconnect structures 170 can beformed over the upper surface 142 of the substrate 106 as well with theinterconnect structures 170 being adjacent the integrated circuit device58.

In one embodiment, an encapsulation material 136 can be used to cover aperipheral portion of the integrated circuit device 58 and a peripheralportion of the interconnect structures 170 using film-assisted moldingsimilar to that discussed above. The peripheral portions are the sidesof the integrated circuit device 58 and the interconnect structures 170that are embedded within the encapsulation material 136. In thisinstance, the upper portions 190 of the interconnect structures 170 andthe upper surface 290 of the integrated circuit device 58 maysubstantially co-planar such that during film-assisted molding of theencapsulation material 136 the upper surface 290 of the integratedcircuit device 58 and the upper portions 190 of the interconnectstructures 170 are exposed.

Next, as shown in FIG. 11, selected upper portions 190 of theinterconnect structures 170A, 170B, 170C, 170D as well as the uppersurface 290 of the integrated circuit device 58 may be treated with adeflashing process similar to that discussed above. The optional solderdeflash or laser deflash may help to remove any mold resin residue thatmay be exposed onto the interconnect structures 170 during film-assistedmolding of the encapsulation material 136. In one embodiment, as shownin FIG. 12, an insulating material 336 may be formed over the uppersurface 290 of the integrated circuit device 58. In other embodiments,the insulating material 336 may be formed over other parts of thepackage 600 as necessary to serve as dielectric primer and preventelectrical shorting. The insulating material 336 may be formed withsimilar processes as the conductive materials 160, 260 described above.For example, the insulating material 336 can be formed by depositing theinsulating material 336 having a first state, and heating the insulatingmaterial 336 from the first state to a second state, where the secondstate is different from the first state. Optionally, the insulatingmaterial 336 may be allowed to disperse or spread out similar to thatdescribed above. In some embodiments, the insulating material 336 mayinclude at least one of dielectric ink, dielectric paste, thermosettingresin, and mixtures thereof.

In one embodiment, the insulating material 336 is a dielectric primermaterial that can be formed by direct writing including withoutlimitation inkjet printing, screen printing or EHD dispensing with adielectric ink. One of the purposes of the insulating material 336 is toprevent electrical short between the subsequently formed conductivelayer 160 and the upper surface 290 of the integrated circuit device 58,which may be conductive.

FIG. 13 includes a top-down view of the next step in the manufacturingprocess of the semiconductor package 600 with a cross-sectional viewthrough A-A of the semiconductor package 600. In one embodiment, aconductive material 160 may be formed over the insulating material 336extending from the upper surface 290 of the integrated circuit device 58to the upper portions 190 of the interconnect structures 170. In someinstances, the conductive material 160 may be formed over the upperportions 190 of the interconnect structures 170 similar to thatdiscussed above. The conductive material 160 can be formed in a similarfashion as that discussed above including depositing the conductivematerial 160 having a third state, optionally allowing the conductivematerial 160 to disperse, followed by heating of the conductive material160 from the third state to a fourth state, where the fourth state isdifferent from the third state. The third state may be similar to thefirst material state above while the fourth state may be similar to thesecond material state above. The conductive material 160 may also havean initial profile and a final profile.

As shown, the conductive material 160 may be indented or slightly offset(e.g., some pullback) from the edges of the insulating material 336 overthe upper surface 290 of the integrated circuit device 58 so as tofurther minimize risk of shorting. Further, as shown, the conductivematerial 160, formed of the conductive material in ink, paste, or liquidform, can conformally form over the structures underneath. In otherwords, the conductive material 160 can follow the shape or contour ofthe insulating material 336 including any angles and crevices thereof,and fill in any of such openings or recesses as necessary in forming theconductive layer 160. The conforming characteristics of the conductivematerial 160 may be further illustrated near the corner of the uppersurface 290 of the integrated circuit device 58 where the conductivematerial 160 “steps down” from the insulating material 336 and makescontact with the encapsulation material 136.

FIG. 14 includes top-down view of a semiconductor package 700 with across-sectional view through A-A of the semiconductor package 700, whichcan be continued from the semiconductor package 600 of FIG. 13 withadditional processing steps. In one embodiment, a second conductivematerial 260 can be formed over the first conductive material 160, wherethe second conductive material 260 and the first conductive material 160have substantially similar geometric footprint. In this embodiment, thegeometric layout of the second conductive layer 260 can follow those ofthe first conductive layer 160 as seen from the top-view as well as thecross-sectional view. And like the first conductive material 160, thesecond conductive material 260 can also conform to the contours andshapes of the first conductive material 160 underneath.

In one embodiment, the first conductive material 160 can serve as a seedlayer while the second conductive material 260 can be the conductivepattern to provide the conductive trace lines along with full area arraytop ball pads. The seed layer 160 may be formed as a conductive ink orpaste by direct writing including without limitation inkjet printing,screen printing or EHD dispensing, the formation being carried outwithout the use of photolithography and/or removal of photoresist.Further, the formation can be carried out without any etching of theconductive material 160. In some embodiments, the second conductivematerial 260 can be formed by electroplating or electro-less plating. Inother embodiments, the second conductive material 260 can be formed bythe printing processes described above similar to those for the firstconductive material 160.

FIG. 15 includes top-down view of a semiconductor package 800 with across-sectional view through A-A of the semiconductor package 800, whichcan be continued from the semiconductor package 600 of FIG. 13 withadditional processing steps. In one embodiment, an isolating material436 can be formed over the upper surface 290 of the integrated circuitdevice 58. In this instance, a first portion of the isolating material436 can be formed over the conductive material 160 while a secondportion of the isolating material 436 can be formed in between andadjacent the conductive material 160. In general, the first portion ofthe isolating material 436 formed over the conductive material 160 aremore directed to the trace lines, e.g., the conductive lines couplingthe interconnect structures 170 to the insulating material 336 over theintegrated circuit device 58. The second portion of the isolatingmaterial 436 formed in between and adjacent the conductive material 160are those adjacent and in between the interconnect structures 170 aboutthe peripheral of the package 800. This is best illustrated on the twoperipheral sides of the cross-sectional view.

In one embodiment, the isolating material 436 may be similar to that ofthe insulating material 336 including at least one of dielectric ink,dielectric paste, thermosetting resin, and mixtures thereof. In someembodiments, the isolating material 436 can be formed with similartechniques as those above for the conductive material 160 or theinsulating material 336. For example, the isolating material 436 can beinitially deposited, optionally be allowed to disperse or spread, andsubsequently heated to form the desired structure and final profile. Inother embodiments, the isolating material 436 can be solder maskmaterial formed by photolithography or direct writing with dielectricink. In one embodiment, the package 700 of FIG. 14 can be combined withthe current package 500 such that the isolating material 436 can beformed over the upper surface 290 of the integrated circuit device 58where a portion is over two conductive layers 160, 260 while anotherportion is in between and adjacent to. In some examples, the isolatingmaterial 436, formed of the isolating material in ink, paste, or liquidform, can be conformally formed over the structures underneath. In otherwords, the isolating material 436 can follow the shape or contour of theconductive layers 160, 260 including any angles and crevices thereof,and fill in any of such openings or recesses as necessary in forming theisolating layer 436.

FIG. 16 includes top-down view of a semiconductor package 650 with across-sectional view through A-A of the semiconductor package 650, whichis in essence substantially similar to the semiconductor package 600 ofFIG. 13 with the exception that the interconnect structure 170 includesa single layer 144. In this package 650, the interconnect structure 170is a standard solder ball with only a single core layer 144. There is noouter layer in this example. The interconnect structure 170 can beformed by traditional solder ball formation techniques. Furthermore, theinterconnect structure 170 can be implemented in other packages 700, 800as well.

FIG. 17 is a cross-sectional view of a semiconductor package accordingto another embodiment of the present disclosure. As shown, asemiconductor package 258 having an integrated circuit device 158therein can be mounted over an existing semiconductor package 300. Inthis instance, the semiconductor package 300 is that of FIG. 6. Thesemiconductor package 258 can be mounted over the conductive layer 160of the semiconductor package 300 via a plurality of internalinterconnects 212. The internal interconnects 212 may be similar tothose of the internal interconnects 110 described above. Once thepackage-on-package (PoP) structure has been formed, both the integratedcircuit devices 58, 158 may be in electrical communication with theexternal interconnects 112. For example, the integrated circuit device58 may be in communication with the external interconnects 112 throughsignal lines within the substrate 106. Meanwhile, the integrated circuitdevice 158 may be in communication with the external interconnects 112through the internal interconnects 212 as well as the conductive layer160. Although only the package 300 of FIG. 6 is shown, it will beunderstood that the upper semiconductor package 258 can be mounted overeach of the various packages 350, 400, 500, 600, 650, 700, 800 disclosedin all the figures of the current disclosure.

FIG. 18 is a flow diagram 900 of the methods of forming conductive andinsulating layers for semiconductor devices and packages. In oneembodiment, a method of forming conductive and insulating layers forsemiconductor packages includes providing a substrate having an uppersurface and a lower surface, where the lower surface is opposite theupper surface as indicated in step 902. Next, a first integrated circuitdevice can be mounted over the upper surface of the substrate in step904. Next, an interconnect structure can be mounted over the uppersurface of the substrate, where the interconnect structure is adjacentthe first integrated circuit device in step 906. Although theinterconnect structure is mounted after the integrated circuit device,the steps 904, 906 may be reversed where the interconnect structure ismounted before the integrated circuit device. Next, the first integratedcircuit device and portions of the interconnect structure can be coveredwith an encapsulation material in step 908. The covering step 908 doesleave an upper portion of the interconnect structure exposed.

A first conductive material can be formed over the upper portion of theinterconnect structure and the encapsulation material in step 910. Theforming step can include the following sub-steps: (i) depositing thefirst conductive material having a first state in step 1010, where thefirst conductive material includes at least one of silver (Ag), platinum(Pt), gold (Au), copper (Cu), carbon nanotube (CNT), graphene, organicmetal, and mixtures thereof. Next, the first conductive material can beheated from the first state to a second state, where the second state isdifferent from the first state in step 1020. Optionally, the conductivematerial can disperse or be allowed to disperse in step 1030. In anotherembodiment, to enhance the dispersion step 1030, the upper portion ofthe interconnect structure can be treated with hydrophilic plasma instep 1040 prior to the forming steps 1010, 1020, 1030.

In one embodiment, the method further includes mounting a semiconductorpackage over the first conductive material in step 912. In thisembodiment, the semiconductor package includes a second integratedcircuit device. In another embodiment, the method further includesforming a plurality of external interconnects on the lower surface ofthe substrate in step 914. In this embodiment, the externalinterconnects is in communication with at least one of the firstintegrated circuit device and the second integrated circuit device.Although the formation of the external interconnects are disclosed instep 914, it is also possible that the external interconnects can beformed in step 924 during the mounting steps 904, 906.

In one embodiment, the method further includes treating the upperportion of the interconnect structure with a deflashing process in step922 after the covering step 908 but before the forming step 910. Inanother embodiment, the method further includes forming a secondconductive material over the first conductive material in step 916. Inthis embodiment, the second conductive material and the first conductivematerial can have substantially similar geometric footprint.

In one embodiment, a method of forming conductive and insulating layersfor semiconductor packages can be substantially similar to that aboveincluding: providing a substrate in step 902, mounting a firstintegrated circuit device and an interconnect structure over thesubstrate in steps 906, 908. The first integrated circuit device and theinterconnect structure can be covered with an encapsulation material instep 908 with a conductive material formed thereover in step 910. Theconductive material can be formed with similar materials and processesas disclosed above and in steps 1010, 1020, 1030 and 1040. In oneembodiment, the method further includes forming an isolating materialover the encapsulation material in step 918. In this embodiment, a firstportion of the isolating material can be formed over the conductivematerial while a second portion of the isolating material can be formedin between and adjacent the conductive material. If the process had beensubjected to two conductive material deposition steps 910, 916, theisolating material can be formed over both conductive materials, as wellas in between and adjacent thereto. In some embodiments, the isolatingmaterial includes at least one of dielectric ink, dielectric paste,thermosetting resin, and mixtures thereof.

Like above, a semiconductor package can be mounted over the conductivematerial in step 912, where the semiconductor package includes a secondintegrated circuit device, while a plurality of external interconnectscan be formed on the lower surface of the substrate in step 914 forcommunicating with either the first integrated circuit device or thesecond integrated circuit device. The upper portion of the interconnectstructure can be treated with a deflashing process in step 922, which isafter the covering step 908 but before the forming step 910.

In one embodiment, a method of forming conductive and insulating layersfor semiconductor packages can be substantially similar to that aboveincluding: providing a substrate in step 902, mounting a firstintegrated circuit device and an interconnect structure over thesubstrate in steps 906, 908. A peripheral portion of the firstintegrated circuit device and a peripheral portion of the interconnectstructure can be covered with an encapsulation material in step 908.Doing so leaves an upper surface of the first integrated circuit deviceand an upper portion of the interconnect structure exposed. Next, aninsulating material can be formed over the upper surface of the firstintegrated circuit device in step 920.

In one embodiment, the insulating material can be formed in similarfashion as that of the conductive material as disclosed above and insteps 1010, 1020, 1030 and 1040. For example, the forming step 920 caninclude the following sub-steps: (i) depositing the insulating materialhaving a first state in step 1010, where the insulating materialincludes at least one of dielectric ink, dielectric paste, thermosettingresin, and mixtures thereof. Next, the insulating material can be heatedfrom the first state to a second state, where the second state isdifferent from the first state in step 1020. Optionally, the insulatingmaterial can disperse or be allowed to disperse in step 1030. In anotherembodiment, to enhance the dispersion step 1030, the upper surface ofthe first integrated circuit device and an upper portion of theinterconnect structure can be treated with hydrophilic plasma in step1040 prior to the forming steps 1010, 1020, 1030.

In one embodiment, the next step includes forming the first conductivematerial over the insulating material in step 910, where the firstconductive material extends from the upper surface of the firstintegrated circuit device to the upper portion of the interconnectstructure. In this instance, the first conductive material can be formedwith similar materials and processes as disclosed above and in steps1010, 1020, 1030 and 1040. In this instance, the first conductivematerial can be deposited at a third state in step 1010, and heated instep 1020 from the third state to a fourth state, where the fourth stateis different from the third state.

Like above, a semiconductor package can be mounted over the conductivematerial in step 912, where the semiconductor package includes a secondintegrated circuit device, while a plurality of external interconnectscan be formed on the lower surface of the substrate in step 914 forcommunicating with either the first integrated circuit device or thesecond integrated circuit device. The upper portion of the interconnectstructure can be treated with a deflashing process in step 922, whichcan take place after the forming step 920 but before the forming step910. In another embodiment, the method further includes forming a secondconductive material over the first conductive material in step 916. Inthis embodiment, the second conductive material and the first conductivematerial can have substantially similar geometric footprint.

In one embodiment, a method of forming conductive and insulating layersfor semiconductor packages can be substantially similar to that aboveincluding: providing a substrate in step 902, mounting a firstintegrated circuit device and an interconnect structure over thesubstrate in steps 906, 908. Peripheral portions of the first integratedcircuit device and the interconnect structure can be covered with anencapsulation material in step 908 leaving an upper surface of the firstintegrated circuit device and an upper portion of the interconnectstructure exposed. Next, an insulating material can be formed over theupper surface of the first integrated circuit device in step 920. Theinsulating material can be formed with similar materials and processesas disclosed above and in steps 1010, 1020, 1030 and 1040. Next, a firstconductive material can be formed over the insulating material in step910, where the first conductive material extends from the upper surfaceof the first integrated circuit device to the upper portion of theinterconnect structure. The first conductive material can be formed withsimilar materials and processes as disclosed above and in steps 1010,1020, 1030 and 1040. In this instance, the first conductive material canbe deposited at a third state in step 1010, and heated in step 1020 fromthe third state to a fourth state, where the fourth state is differentfrom the third state.

In one embodiment, the next step includes forming an isolating materialover the upper surface of the first integrated circuit device in step918. In this embodiment, a first portion of the isolating material canbe formed over the conductive material while a second portion of theisolating material can be formed in between and adjacent the conductivematerial. If the process had been subjected to two conductive materialdeposition steps 910, 916, the isolating material can be formed overboth conductive materials, as well as in between and adjacent thereto.In some embodiments, the isolating material includes at least one ofdielectric ink, dielectric paste, thermosetting resin, and mixturesthereof.

Like above, a semiconductor package can be mounted over the conductivematerial in step 912, where the semiconductor package includes a secondintegrated circuit device, while a plurality of external interconnectscan be formed on the lower surface of the substrate in step 914 forcommunicating with either the first integrated circuit device or thesecond integrated circuit device. The upper portion of the interconnectstructure can be treated with a deflashing process in step 922 after theforming step 920 but before the forming step 910.

The currently disclosed embodiments are able to deliver low costpackaging solutions including upper fan-in solution for stackedpackages. In other words, an upper package with smaller or reducedfootprint can be mounted over the various packages described herein. Thecost savings can be realized by eliminating the need for expensivedual-sided substrates or additional substrates or interposers. Thepackage structures are also able to achieve moderate warpage.Furthermore, thin package profiles can be achieved with fine pitchinterconnects can be formed by direct writing processes includingwithout limitation inkjet, screen printing or EHD dispensing for formingthe conductive, insulating and isolating layers. In some instances, thelayer patterns can be single layer or multi-layered. The upperinterconnect structures can be single layer solder balls ormulti-layered solder balls with metal core or polymer with metal platedcore solder balls. With multi-layered solder balls, the collapse may beless during reflow versus single layer solder balls.

Although the current description has been described in detail withreference to several embodiments, additional variations andmodifications exist within the scope and spirit of the disclosure.

What is claimed:
 1. A method of making a semiconductor device,comprising: providing a substrate; disposing a semiconductor die overthe substrate; depositing an encapsulant around the semiconductor die;forming an insulating material over a portion of the encapsulant and aportion of the semiconductor die using a printing process; and forming afirst conductive layer over the insulating material.
 2. The method ofclaim 1, further including forming an interconnect structure over thesubstrate adjacent to the semiconductor die.
 3. The method of claim 1,wherein forming the insulating material includes: depositing theinsulating material in a viscous state; and heating the insulatingmaterial from the viscous state to a non-viscous state.
 4. The method ofclaim 1, wherein the insulating material includes dielectric ink,dielectric paste, or thermosetting resin.
 5. The method of claim 1,further including forming a second conductive layer over the firstconductive layer.
 6. The method of claim 1, further including forming aninsulating layer over the first conductive layer.
 7. A method of makinga semiconductor device, comprising: providing a semiconductor die;depositing an encapsulant around the semiconductor die; printing aninsulating material over a portion of the encapsulant and a portion ofthe first semiconductor die; and forming a first conductive layer overthe insulating material.
 8. The method of claim 7, further including:providing a substrate, wherein the semiconductor die is disposed overthe substrate; and forming an interconnect structure over the substrateadjacent to the semiconductor die.
 9. The method of claim 7, whereinforming the insulating material includes: depositing the insulatingmaterial in a viscous state; and heating the insulating material fromthe viscous state to a non-viscous second state.
 10. The method of claim7, wherein the insulating material includes dielectric ink, dielectricpaste, or thermosetting resin.
 11. The method of claim 7, furtherincluding printing the first conductive layer over the insulatingmaterial.
 12. The method of claim 7, further including forming a secondconductive layer over the first conductive layer.
 13. The method ofclaim 7, further including forming an insulating layer over the firstconductive layer.
 14. A semiconductor device, comprising: a substrate; asemiconductor die disposed over the substrate; an encapsulant depositedaround the semiconductor die; an insulating print material formed over aportion of the encapsulant and a portion of the semiconductor die; and afirst conductive layer formed over the insulating print material. 15.The semiconductor device of claim 14, further including an interconnectstructure formed over the substrate adjacent to the semiconductor die.16. The semiconductor device of claim 14, wherein the insulating printmaterial includes dielectric ink, dielectric paste, or thermosettingresin.
 17. The semiconductor device of claim 14, wherein the firstconductive layer includes conductive ink or conductive liquid.
 18. Thesemiconductor device of claim 14, further including a second conductivelayer formed over the first conductive layer.
 19. The semiconductordevice of claim 14, further including an insulating layer formed overthe first conductive layer.
 20. A semiconductor device, comprising: asemiconductor die; an encapsulant deposited around the semiconductordie; an insulating print material over a portion of the encapsulant anda portion of the first semiconductor die; and a first conductive layerformed over the insulating print material.
 21. The semiconductor deviceof claim 20, further including: a substrate, wherein the semiconductordie is disposed over the substrate; and an interconnect structure formedover the substrate adjacent to the semiconductor die.
 22. Thesemiconductor device of claim 20, wherein the insulating print materialincludes dielectric ink, dielectric paste, or thermosetting resin. 23.The semiconductor device of claim 20, wherein the first conductive layerincludes conductive ink or conductive liquid.
 24. The semiconductordevice of claim 20, further including a second conductive layer formedover the first conductive layer.
 25. The semiconductor device of claim20, further including an insulating layer formed over the firstconductive layer.